One-component product offering excellent adhesion to most of plastic surfaces used in car bumpers manufacturing (polypropylene, polycarbonate, ABS, Pocan, xenoy, rigid polyurethane, fiberglass reinforced polyester, etc. except for polyethylene and mixture containing this stuff). It features fast drying, high adhesion, excellent resistance to washing and weathering; semi-matt appearance like the original bumpers. It can be used as a finishing treatment or as adhesion primer, also before applying the polyester filler FIBRATO code 3105.
Technical data
Binder : blend of alkyd and acrylic resins
Dry film appearance : semi-matt - 15 ÷ 20 gloss (Gardner 60°)
Specific gravity : 1.12 kg/l ( ± 0.02)
Viscosity : 2000 ÷ 3000 mPa.s Brookfield RVT rpm 50 s 5
Practical cover rate : 3 ÷ 5 m²/l according the applied thickness.
Storage life @ 20°C (68°F) : 24 months in original sealed container.
The product is compliant with Directive 2004/42/CE-IIB(c) maximum VOC limit value: 540 g/l
Application note Substrate preparation : Surface to be treated must be dry, clean and free from oil, bitumen and mud stains. Clean off silicon or polishing wax traces using a wipe soaked with ANTISILICONE code 1618.
Product preparation : Stir well to even colour and consistency.
Application method : - air mix spray gun with nozzle ∅ 1.7 ÷ 1.9 mm and pressure of 2 ÷ 3 bar.
Reduction : To obtain a thick texture: do not reduce. Add 10% of DILUENTE NITRO ANTINEBBIA (cellulose thinner) code 1616 for a normal texture or if used as a primer.
Suggested thickness : 50 ÷ 100 μm dry film high thickness is not needed.
Air drying @ 20°C
Touch dry : 30 minutes
with thickness of 80 ÷ 100 μm Through drying : 8 hours
Recoatable : after 4 ÷ 6 hours